Preparation and characterization of NaY zeolitein a rotating packed bed Open Access
文章信息
Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing100029, China; Department of Chemical and Pharmaceutical Engineering, Hebei University of Science and Technology, S;Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing100029, China;Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing100029, China;Research Center of the Ministry of Education for High Gravity Engineering and Technology, Beijing University of Chemical Technology, Beijing100029, China
文章摘要
with a specific composition was used as the structure-directing agent. The as-synthesized NaY Zeolite was
characterized with scanning electron microscopy (SEM), X-ray diffraction (XRD) and specific surface area
(BET). The characterization result showed that the NaY Zeolite had a particle size of approximately 200 nm,
n(SiO2)/n(Al2O3) ratio of 5.03, crystallinity of 96% and specific surface area of 714 m2/g. The experimental
results indicated that the structure of NaY Zeolite was related to the synthesis conditions (such as reactors,
crystallization time and so on). The micromixing efficiency was proven to be the most important factor for
synthesis of NaY Zeolite in the high-gravity environment in RPB.